Flakes
| Глоссарий терминов по технологиям неразрушающего контроля (NDT) |
- Short discontinuous internal fissures in ferrous metals attributed to stresses produced by localized transformation and decreased solubility of hydrogen during cooling after hot working. in a fractured surface, flakes appear as bright silvery areas; on an etched surface they appear as short, discontinuous cracks. also called “shatter cracks and snowflakes.”
- Short discontinuous internal fissures in ferrous metals attributed to stresses produced by localized transformation and/or decreased solubility of hydrogen during cooling usually after hot working. on a fractured surface, flakes appear as bright silvery areas; on an etched surface, flakes appear as short, discontinuous cracks.2,5
- Short discontinuous internal fissures in ferrous metals attributed to stresses produced by localized transformation and/or decreased solubility of hydrogen during cooling usually after hot working. flakes appear as bright silvery areas (fish eyes) on an otherwise ductile fracture surface; flakes appear as short, discontinuous cracks on a polished and etch cross section. see also hydrogen embrittlement.
|
Флокен, русский
Дефект в виде разрыва тела отливки под влиянием растворенного в стали водорода и внутренних напряжений, проходящего полностью или частично через объемы первичных зерен аустенита [10].
|
Discontinuous, английский
A прерывистый morpheme
Attributed, английский
To be identified as the work of a particular author.
Transformation, немецкий
Solubility, английский
Растворимость
|
Back reflection (ut), английский
Signal from the far boundary of the test part.
Protective material (rt), английский
Shielding material used for the purpose of radiation protection.
|
|
|
|
|
|
|